Polished talc microbeads

ABSTRACT

Polished talc microbeads, i.e. polished talc particles with a largest average diameter of less than 500 μm and methods for the preparation thereof, which microbeads are especially suitable to be use as an alternative for plastic microbeads used in cosmetics and personal hygiene products. Body scrubs, tooth pastes and soaps comprising the present polished talc microbeads. The use of polished talc microbeads with a talc content of more than 70% (w/w) and a largest diameter of less than 500 μm as a substitute for plastic microbeads in cosmetics and personal hygiene products.

The present invention relates to polished talc microbeads, i.e. polished talc particles with a largest average diameter of less than 500 μm and to methods for the preparation thereof. The present polished talc microbeads are especially suitable to be use as an alternative for plastic microbeads, such as polyethylene microbeads, used in cosmetics and personal hygiene products. Accordingly, the present invention additionally relates to body scrubs, tooth pastes and soaps comprising the present polished talc microbeads.

Presently, microbeads are solid plastic particles of less than 0.5 millimetres in their largest dimension. They are generally made of polyethylene but can be of other plastics such as polypropylene and polystyrene. Microbeads have been used in personal care products, cosmetics and toothpastes as well as in biomedical and health science research. Sphericity and particle size uniformity create a ball-bearing effect in creams and lotions, resulting in a silky texture and spreadability. Smoothness and roundness provide lubrication.

Microbeads, after use, are generally washed down the drain and can pass unfiltered through the sewage treatment plants ultimately making their way into rivers and canals, resulting in plastic particle water pollution. The beads can absorb and concentrate pollutants like pesticides and polycyclic hydrocarbons. Microbeads have been found to pollute the Great Lakes in high concentrations, particularly Lake Erie. A study from the State University of New York, found anywhere from 1500 to 1 million microbeads per square mile on the surface of the Great Lakes.

Due to the increase in bans of microbeads in many countries such as the USA and in Europe, many cosmetic companies are phasing out microbeads from their production lines for exfoliates, cleansers and shower gels.

Considering the above, there is a clear need in the art for alternatives of plastic microbeads being readily applicable in cosmetics and personal hygiene products and being environmental friendly.

It is an object of the present invention, amongst other objects, to meet the above need in the art.

This object of the present invention, amongst other objects is met as outlined in the appended claims.

Specifically, this object of the present invention, amongst other objects, is met, according to a first aspect, by the use of polished talc microbeads with a talc content of more than 70% (w/w) such as 80%, 90%, 91%, 92%, 93%, 94%, 95% as 96%, 97%, 98%, 99% and substantially 100%, and a largest diameter of less than 500 μm as substitute for plastic microbeads in cosmetics and personal hygiene products.

The present inventors have surprisingly found that relatively small talc particles, i.e. less than 500 μm, of sufficient purity, i.e. >75% (w/w) can provide a suitable alternative for plastic microbeads. However, such talc particles can only provide an alternative if sufficiently spherical and smooth, or formulated differently, sufficiently polished. According to the invention, such polishing can be readily obtained by adding sieved talc particles of less than 500 μm into a revolving drum and allowing the talc particles to tumble, i.e. to roll over. Although a specific time frame depends on process conditions, suitable time frames to be contemplated are 5 minutes to 2 hours.

Considering the above, the present invention, according to a second aspect, relates to a method for providing polished talc microbeads, the method comprises the steps of:

-   -   a) providing course talc with a talc content of at least 70,         preferably at least 95% and an average largest diameter of         between 1 cm to 10 cm;     -   b) crushing the course talc particles;     -   c) sieving the crushed talc particles through a sieve thereby         obtaining talc particles with an average largest diameter of         less than 500 μm;     -   d) subjecting the sieved talc particles to tumbling thereby         obtaining polished talc microbeads.

According to the present invention, polished talc microbeads with a largest diameter between 500 μm and 250 μm can be used in a body scrub; polished talc microbeads with a largest diameter between 250 μm and 125 μm can be used in a facial scrub; and polished talc microbeads with a largest diameter is between 125 μm and 0.5 μm such as 90 μm can be used in tooth paste, creams and soaps.

According to the present invention, polished talc particles can also be used in a liquid, i.e. water based, soap in an amount of 1% to 5% (w/w) in combination with one or more surfactants in an amount of 1% to 15% (w/w).

According to the present invention, the present polished talc particles can also be used in a dry soap comprising more than 50% (w/w/) of the present polished talc microbeads in combination with one or more surfactants.

The present invention will be further detailed in the following examples of preferred embodiments of the present invention. In the examples, reference is made to a FIG. 1 wherein:

FIG. 1: shows a 30× magnification of the present polished talc microbeads after tumbling (right) and before tumbling (left).

EXAMPLES Example 1: General Preparation of the Polished Talc Microbeads

Coarse talc (hydrated magnesium silicate) of less than 10 cm diameter was subjected to crushing and subsequently sieved to obtain a fractions with 1) an average largest diameter of 500 to 250 μm; 2) an average largest diameter of 250 to 125 μm; 3) an average largest diameter of 125 to 90 μm and 4) an average largest diameter of less than 90 μm. Subsequently, the fractions were added into a rotating drum and allowed to tumble at 60 rpm for 20 minutes in order to polish the talc particles. A representative example of the 500 to 250 μm fraction before (left) and after (right) tumbling is shown in FIG. 1. As can be seen in FIG. 1, tumbling provides smoothness and roundness to the talc particles and, additionally, provides a more spherical shape.

Example 2: Powdered Soap (Dry Soap)

Three formulations of a powdered (dry) soap were prepared by mixing the constituting ingredients in any given order:

Fomulation 1 Amount in Compound percentage (w/w) Function Sodium lauryl sulfoacetate 26 Surfactant Polished talc ad 100 fraction less than 250 μm Sorbitol 5 Humectant Citric acid monohydrate 0.3 Buffer

Formulation 2 Amount in Compound percentage (w/w) Function Sodium lauryl sarcosinate 24.7 Surfactant Polished talc ad 100 fraction less than 250 μm Citric acid 0.3 Buffer Sodium methyl cocoyl 5.2 Surfactant taurate

Formulation 3 Amount in Compound percentage (w/w) Function Sodium lauryl sulfoacetate 23.0 Surfactant Polished talc ad 100 fraction less than 250 μm Citric acid 0.3 Buffer Sodium methyl cocoyl 5.7 Surfactant taurate Sorbitol 5.0 Humectant Allantoin 0.2 Skin soothing and protection Urea 0.3 Skin conditioning

Example 3: Liquid Soap

Formulation liquid soap Amount in Compound percentage (w/w) Function Aqua Ad 100 Solvent Acrylates/C10-30 Alkyl 0.8 Viscosity modifier Acrylate Crosspolymer Sodium Lauroyl  5.13 Surfactant Sarcosinate Sodium Laureth Sulfate 2.7 Surfactant Cocamidopropyl Betaine 0.9 Surfactant Triethanolamine q.s. buffer Polished talc 2.5 fraction less than 250 μm

Manufacturing Procedure:

Heat water of phase A up to 40° C. Add Acrylates/C10-30 Alkyl Acrylate Crosspolymer while stirring and homogenize for 1 to 2 min. to ensure complete hydration. Mix the remained of the ingredients and adjust the pH with triethanolamine to 6.8. Stir with moderate speed until a homogenous gel is obtained.

Appearance: milky homogenous gel pH-Value: 6.8 Viscosity (Brookfield RVDVI, spindle 3, speed 10 rpm) mPa·s: 4500-7000 Stability: more than 3 months. 

1. A cosmetics or personal hygiene product including polished talc microbeads with a talc content of more than 70% (w/w) and a largest diameter of less than 500 μm.
 2. The cosmetics or personal hygiene product according to claim 1, wherein the largest diameter is between 500 μm and 250 μm and the personal hygiene product is a body scrub.
 3. The cosmetics or personal hygiene product according to claim 1, wherein the largest diameter is between 250 μm and 125 μm and the personal hygiene product is a facial scrub.
 4. The cosmetics or personal hygiene product according to claim 1, wherein the largest diameter is between 125 μm and 0.5 μm and the personal hygiene product is a tooth paste, cream or soap.
 5. The cosmetics or personal hygiene product according to claim 1, wherein the personal hygiene product is a liquid soap comprising 1% to 5% (w/w) polished talc microbeads, 1% to 15% (w/w) of one or more surfactants and water up to 100% (w/w).
 6. The cosmetics or personal hygiene product according to claim 1, wherein the personal hygiene product is a dry soap comprised of at least 50% (w/w) polished talc microbeads and at least 15% (w/w) of one or more surfactants.
 7. The cosmetics or personal hygiene product according to claim 1, wherein the cosmetics or personal hygiene product comprises a body scrub comprising polished talc microbeads with a talc content of more than 70% (w/w) with a largest diameter between 500 μm and 250 μm.
 8. The cosmetics or personal hygiene product according to claim 1, wherein the cosmetics or personal hygiene product comprises a facial scrub comprising polished talc microbeads with a talc content of more than 75% (w/w) with a largest diameter between 250 μm and 125 μm.
 9. The cosmetics or personal hygiene product according to claim 1, wherein the cosmetics or personal hygiene product comprises a tooth paste, a cream or a soap comprising polished talc microbeads with a talc content of more than 75% (w/w) with a largest diameter is between 125 μm and 0.5 μm.
 10. A soap comprising: a liquid soap comprising 1% to 5% (w/w) polished talc microbeads, 1% to 15% (w/w) of one or more surfactants and water up to 100% (w/w); or a dry soap comprised of at least 50% (w/w) polished talc microbeads and at least 15% (w/w) of one or more surfactants.
 11. (canceled)
 12. A method for providing polished talc microbeads, the method comprising: a) providing course talc with a talc content of at least 70% and an average largest diameter of between 1 cm to 10 cm; b) crushing the course talc particles; c) sieving the crushed talc particles through a sieve to obtain talc particles with an average largest diameter of less than 500 μm; d) tumbling the sieved talc particles in a tumbler to obtain polished talc microbeads.
 13. The method according to claim 12, wherein said course talc in step a) has a talc content of at least one of: at least 80%, at least 90%, at least 95%, at least 96%, at least 97% at least 98%, at least 99%, or substantially 100%.
 14. The method according to claim 12, wherein step c) talc particles are obtained with an average largest diameter of less than 250 μm or less than 125 μm.
 15. (canceled) 